8 g / 10 min (Test Method: ISO 1133-A (210°C/2.16kg))
1.24 g / cm3 (Test Method: ISO 1183)
PLA is a biobased polymer derived from natural resources and offers a significant reduction in carbon footprint compared to oil-based
plastics. Luminy® L175 is a high heat, high viscosity, PLA homopolymer suitable for film extrusion, thermoforming or fiber spinning.
Compared to standard PLA, these PLA homopolymers have higher melting points and an increased rate of crystallization. As a result,
compounds containing PLA homopolymers are suitable for the production of semicrystalline parts, which exhibit a higher temperature
resistance.